Corrosion behaviors of P110 steel and chromium coating in CO 2-saturated simulated oilfield brine

N Lin, F Xie, J Zhou, X Wu… - Journal of Wuhan University of …, 2011 - Springer
... casing tube) and transportation (pipeline) systems [3-5] . It is acknowledged that when the CO2
dissolves into water, the carbonic acid will form, which is even more corrosive to steel than a
completely dissociated acid at the same pH value [6-8] . The CO2 cor- rosion can cause ...
Related articles

High Temperature Corrosion Problem of Boiler Components in presence of Sulfur and Alkali based Fuels

D Ghosh… - High Temperature Materials and …, 2011 - reference-global.com
... Different damage mechanisms like creep, fatigue, erosion and cor- rosion are becoming operative
during operation and causes material degradation and finally leads to failure [2]. The high
temperature corrosion problem in coal-based power plants is prevalent damage ...
Related articles

Effect of Sealing Treatment on Corrosion Resistance of Plasma-Sprayed NiCrAl/Cr 2 O 3-8 wt.% TiO 2 Coating

J Zhang, Z Wang, P Lin, W Lu, Z Zhou… - Journal of thermal spray …, 2011 - Springer
... lamellae (which depends mainly on spraying parameters), as well as partly or totally semi-molten
particles and entrapped gas (Ref 1-4). The structural defects allow paths for electrolytes from
the outer surface to the substrate, which deteriorate the cor- rosion resistance of the ...
Related articles - All 6 versions

Adsorption properties and inhibition of mild steel corrosion in hydrochloric acid solution by ceftobiprole

AK Singh… - Journal of Applied Electrochemistry, 2011 - Springer
... The inhibitors influence the kinetics of the electrochemical reactions which constitute the
cor- rosion process and thereby modify the metal dissolution in acids. The existing data show
that most organic inhibitors act by adsorption on the metal surface. ...
Cited by 2 - Related articles - All 3 versions

A Comparative Study of the Corrosion Behavior of Three Stainless Steels in an Eutectic (Li, Na, K) 2CO3 Melt with and without (Na, K) Cl Additives at 973 K in Air

CL Zeng… - High Temperature Materials and …, 2011 - reference-global.com
... The addition of chlorides to carbonates melt accelerated the cor- rosion of the steels, especially
310 steel, producing scales with more porosity. Keywords. Stainless steels, (Li,Na,K)2CO3,
(Na,K)Cl, molten salts corrosion. PACS®(2010). 81.65-Mq. 1 Introduction ...
Related articles

联系我们 | 站点地图 | 友情链接 | 授权代理商 | 加入我们

© 2010-2024 中国: LetPub上海分公司    网站备案号：沪ICP备10217908号-1    沪公网安备号：31010402006960

增值电信业务经营许可证：沪B2-20211595

礼翰商务信息咨询（上海）有限公司      办公地址：上海市徐汇区漕溪北路88号圣爱大厦1803室

United States: Tel: 1-781-202-9968 Address: 400 5th Ave, Suite 530, Waltham, Massachusetts 02451